PolyAcryloNitrile is calcinated to PAN type carbon fibre in 3 steps: stabilisation oxidation at 300°C, carbonization at 1600°C then graphitization at 3000°C.

W. Büchner, R. Schliebs, G. Winter, K.H. Büchel, Industrial Inorganic Chemistry, VCH, 1989

         